| Place of Origin: | China |
| Brand Name: | LH-tool® |
| Certification: | ISO9001:2008 Standard |
| Model Number: | LH105AB |
| Minimum Order Quantity: | 200kgs |
|---|---|
| Price: | Negotiation |
| Packaging Details: | Standard Carton Packing |
| Delivery Time: | 15 Days |
| Payment Terms: | T/T |
| Supply Ability: | 30 Tons per Month |
| Materials: | Epoxy Resin | Color: | Brown |
|---|---|---|---|
| Package: | 2kg 10kg 20kg | Density: | 0.7-0.8,1.0-1.6 |
| Hardness: | 70-80,85-90 | Mixing Ratio: | 1 More Than 1 |
| High Light: | model glue,epoxy bonding adhesive |
||
Brown LH105 Resin Modeling Adhesives Epoxy Resin Materials CNC Machining process
Method of use
1. Respectively take agent 1 A and 1 B mix and stir to mix well.1 (weight ratio)
2. AB coating on the bonding agent mixture, and give us stick light pressure.
3. A glue adhesive items to shift of the banned or move in at least 10 minutes, otherwise it will seriously affect the bonding effect.
4. A glue adhesive items should be at least 4 hours before they can normal use, otherwise the curing effect and adhesive life would be affected.
5. Low temperature curing speed will slow down.
6. the appropriate surface treatment: then body surface of grease or oil to clear or grinding, remove foreign bodies to strengthen the bonding effect.
Matters needing attention
1. A, B two agent shall be stored in shady and cool place, two doses not piled up at the same time.
2. A, B two agent such as A large number of mix, causes rapid solidification of danger, should be especially careful, according to the usage.
3. After use, such as skin touch/consignment agent, the application of soap to clean.
4. Coated tools or containers are mixed, to shorten the service life.
Note: the product packaging in each group 2 kg, each box 10, will be A and B glue can be used according to the ratio of 1:1 and stir well,
Introduction
| Material | 108A | 108B | Mixed |
| Description | epoxy resin | curing agent | |
| mixing ration | 1 | 1 | |
| Color: | Beige | Yellow | Yellow |
| mixed time:500g,25°(min) | 30 | ||
| curing time before machining(20-25mm) (hours) | 60minutes | ||
| Hardness(Shore D): | 70-80 | ||
| Temperature Resistance(°C): | 100-150 | ||
| Compressive Strength(N/mm²): |
290-320(kg/cm2) |
||
| Flexural Strength(N/mm²): |
102(kg/cm2) |
Characteristics
easily shaped and machined,fine surface structure
Applications:
yacht model,benchmark model, system and sand-cast model, rapid prototype,etc.
Contact Person: 谭琳
Tel: +8613533033735
Epoxy Tooling Block Modeling Board For Making Main mould / Automobile Model
Polyurethane Model Making Board , CNC Tooling Board Block Lightweight
Precision Polyurethane Epoxy Tooling Board For Prototyping / Modeling No Shrinkage
Epoxy Resin High Density Model Board , Epoxy Tooling Block Multi Color Available
Brown Color Polyurethane Tooling Board For Model Making 750x500mm 1500x500mm
High Toughness Polyurethane Model Board , Epoxy Resin Tooling Board
CNC Machinable Polyurethane Tooling Board 0.77 Density High Hardness
Polyurethane Materials Epoxy Tooling Block High Density For Mould Pattern Making
Brown Polyurethane High Density Model Board 1000mm x 500mm x 50/75/100mm
Polyurethane High Density Model Board For Rapid Prototyping And Model Making
Red Color Rigid Epoxy Tooling Board , Polyurethane Pattern Making Board
Model Making High Density Model Board Polyurethane Tooling Board Grey Color